LORD® 810 Low Read-Through (LRT) acrylic adhesive when cured with LORD® Accelerator 20GB creates a flexible adhesive system for bonding metals, such as aluminum, galvanized steel and CRS, and engineered plastics, such as PC-ABS. LORD® 810 adhesive in combination with LORD® Accelerator 20GB delivers fast cure speed and strong bonding with minimal bondline read through (BLRT).

LORD® Accelerator 20GB allows precise control of the adhesive bondline thickness due to its content of glass beads. For further detailed information, refer to the LORD® Accelerator 20GB data sheet.
Unit of Measure

Typical Properties

Appearance

 N/A Black Paste

Brookfield Viscosity at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature

 N/A 40000 to 130000 cP

Density

 N/A 7.80 to 8.10 lb/gal935 to 970 kg/m³

Note for Typical Properties

 N/A Data is typical and not to be used for specification purposes.

Specifications

Flash Point Temperature

 N/A 59 ºF15 ºC

Shelf Life

 N/A 1 y

Typical Cured Properties

Typical Cured Hardness

 N/A 40 Shore "D"

Typical Cured Tensile Strength at Break

 N/A 841 psi5.8 MPa

Typical Cured Elongation

 N/A 190 %

Typical Cured Glass Transition Temperature (Tg)

 N/A 109 ºF43 ºC

Note for Typical Cured Properties

 N/A Data obtained using LORD® 810 adhesive/Accelerator 20GB cured for 24 hours at room temperature. Data is typical and not to be used for specification purposes.

Typical Post-Baked Properties

Typical Post-Baked Hardness

 N/A 69 Shore "D"

Typical Post-Baked Tensile Strength at Break

 N/A 2088 psi14.4 MPa

Typical Post-Baked Elongation

 N/A 22 %

Typical Post-Baked Glass Transition Temperature (Tg)

 N/A 136 ºF58 ºC

Note for Typical Post-Baked Properties

 N/A Data obtained using LORD® 810 adhesive/Accelerator 20GB cured for 24 hours at room temperature then baked at 140 ºF (60 ºC) for 500 hours. Data is typical and not to be used for specification purposes.

Typical Properties of Adhesive Mixed with Recommended Accelerator

Mix Ratio by Weight, Adhesive to Accelerator

 N/A 1.1:1

Mix Ratio by Volume, Adhesive to Accelerator

 N/A 2:1

Working Time at 70 Degree Fahrenheit (ºF) (21 Degree Celsius (ºC)) Temperature

 N/A 8 to 12 minutes

Time to Handling Strength at 70 Degree Fahrenheit (ºF) (21 Degree Celsius (ºC)) Temperature

 N/A 20 to 25 minutes

Mixed Appearance

 N/A Gray Paste

Cured Appearance

 N/A Gray

Note for Typical Properties of Adhesive Mixed with Recommended Accelerator

 N/A Data is typical and not to be used for specification purposes.

Shelf Life/Storage

Shelf Life/Storage

 N/A Shelf life is one year when stored below 77 ºF (25 ºC) in original, unopened container. Storage temperatures of 40-60 ºF (4-15 ºC) are recommended. If stored cold, allow product to return to room temperature before using. Protect from exposure to direct s

Features

Aesthetics

 N/A Bonds thin and flexible substrates with little to no bondline read-through.

Convenient

 N/A Requires little or no substrate preparation for bonding metals and plastics.

Environmentally Resistant

 N/A Resists dilute acids, alkalis, solvents, greases, oils and moisture; provides excellent resistance to indirect UV exposure and weathering.

Temperature Resistant

 N/A Performs at temperatures from -40 ºF to +300 ºF (-40 ºC to +149 ºC).

Non-Sag

 N/A Remains in position when applied on vertical or overhead surfaces, allowing for greater process flexibility.

Applications

Surface Preparation

 N/A Remove grease, loose contamination or poorly adhering oxides from metal surfaces. Normal amounts of mill oils and drawing compounds usually do not present a problem in adhesion. Most plastics require a simple cleaning before bonding. Some may require abrading for optimum performance.

Applying

 N/A Apply the mixed adhesive to bond surfaces using a handheld cartridge or automatic meter/mix/ dispense equipment. Contact your LORD® representative if assistance is needed using this equipment.

Mixing

 N/A Mix LORD® 810 adhesive with LORD® Accelerator 20GB at a ratio of 2:1, adhesive to accelerator, by volume. Even color distribution visually indicates a thorough mix. Once mixed, the adhesive system cures rapidly.

Curing

 N/A Initial cure (90% cure strength) is achieved after 30 minutes at room temperature [77 ºF (25 ºC)]. Complete cure requires 24 hours at room temperature. Mating surfaces must be held in contact during the entire curing process. Cure rate can be accelerated by applying modest heat [<105 ºF (<66 ºC)]

Cleanup

 N/A Clean equipment and tools prior to the adhesive cure with solvents such as isopropyl alcohol, acetone or methyl ethyl ketone (MEK). Once adhesive is cured, heat the adhesive to 400 ºF (204 ºC) or above to soften the adhesive. This allows the parts to be separated and the adhesive to be more easily removed.

Additional Information

Additional Information

 N/A Values stated in this technical data sheet represent typical values as not all tests are run on each lot of material produced.

Information provided herein is based upon tests believed to be reliable. In as much as LORD® Corporation has no control over the manner in which others may use this information, it does not guarantee the results to be obtained. In addition, LORD® Corporation does not guarantee the performance of the product or the results obtained from the use of the product or this information where the product has been repackaged by any third party, including but not limited to any product end-user. Nor does the company make any express or implied warranty of merchantability or fitness for a particular purpose concerning the effects or results of such use.

LORD® and "Ask Us How™" are trademarks of LORD® Corporation or one of its subsidiaries.

LORD® provides valuable expertise in adhesives and coatings, vibration and motion control, and magnetically responsive technologies. Our people work in collaboration with our customers to help them increase the value of their products. Innovative and responsive in an ever-changing marketplace, we are focused on providing solutions for our customers worldwide. Ask Us How™.